PPS-CF is a composite material made from carbon fiber-reinforced polyphenylene sulfide. The combination of PPS resin and carbon fiber gives PPS-CF exceptional properties, including excellent resistance to solvents, corrosion, heat, and flames. Additionally, it offers superior strength, stiffness, and dimensional stability, making it a specialized engineering plastic that meets the demands of unique and challenging applications.

Product Features

Ultra-High Heat Resistance
Top-tier Flame Retardancy
Peerless Mechanical Properties
Solvent and Chemical Resistance
Ultra-Low Water Absorption
Comes with Cardboard Spool
Diameter: 1.75 mm +/- 0.05 mm

PPS-CF	PET-CF	PA6-CF
Composition	Polyphenylene sulfide (PPS), Carbon Fiber	Polyethylene terephthalate (PET), Carbon Fiber	Nylon6 (PA6), Carbon Fiber
AMS & AMS lite Compatibility	Not Compatible	Not Compatible	Not Compatible
Dry before Use	Required	Required	Required
Sealed during Printing	Sealed with desiccant	Sealed with desiccant	Sealed with desiccant
Printer Type	Enclosed	Enclosed (Recommended) / Open-frame	Enclosed
Nozzle	Hotend with Hardened Steel 0.4mm / 0.6mm (recommended) / 0.8 mm	Hotend with Hardened Steel 0.4mm / 0.6mm (recommended) / 0.8 mm	Hotend with Hardened Steel 0.4mm / 0.6mm (recommended) / 0.8 mm
Nozzle Temperature	310 - 340 ℃	260 - 300 ℃	260 - 300 ℃
Bed Temperature	100 - 120 ℃	80 - 110 ℃	100 - 110 ℃
Toughness (Impact Strength - XY, Dry State)	27.8 kJ/m²	36.0 kJ/m²	40.3 kJ/m²
Toughness (Impact Strength - XY, Wet State)	27.8 kJ/m²	37.3 kJ/m²	57.2 kJ/m²
Strength (Bending Strength - XY, Dry State)	142 MPa	131 MPa	151 MPa
Strength (Bending Strength - XY, Wet State)	142 MPa	127 MPa	95 MPa
Layer Strength (Bending Strength - Z, Dry State)	36 MPa	49 MPa	80 MPa
Layer Strength (Bending Strength - Z, Wet State)	36 MPa	46 MPa	45 MPa
Stiffness (Bending Modulus - XY, Dry State)	7160 MPa	5320 MPa	5460 MPa
Stiffness (Bending Modulus - XY, Wet State)	7160 MPa	5240 MPa	3560 MPa
Layer Adhesion (Impact Strength - Z, Dry State)	2.8 kJ/m²	4.5 kJ/m²	15.5 kJ/m²
Heat Resistance (HDT, 0.45 MPa, Dry State)	264 ℃	205 ℃	186 ℃
Saturated Water Absorption Rate (25 °C, 55% RH)	0.05%	0.37%	2.35%